Author:
Niebuhr R.,Bachem K. H.,Behr D.,Hoffmann C.,Kaufmann U.,Lu Y.,Santic B.,Wagner J.,Arlery M.,Rouviere J. L.,Jürgensen H.
Abstract
ABSTRACTAlGaN/GaN single quantum wells (QW) have been grown on 2” sapphire substrates (c-plane) by metal-organic chemical vapor deposition (MOCVD). The well width was varied between 20 and 40 Å for barriers containing 4 % and 16 % of aluminium. Cathodoluminescence (CL) and Photoluminescence (PL) spectra of the samples show, as expected, a shift of the quantum well emission to higher energies with decreasing well width, whereas the barrier luminescence stays at constant energy. Examination of the QWs by resonant Raman spectroscopy tuned to the gap of the well, clearly shows the GaN A1(LO) phonon besides the AlGaN A1(LO) phonon from the barrier. For a well width of 20 Å we observe a shift of the A1(LO) GaN phonon indicating a certain degree of intermixing at the GaN/AlGaN interface. Atomic Force Microscopy (AFM) reveals that the layers are growing in a 2-dimensional step flow growth mode with step heights of 3 and 6 Å corresponding to mono- and biatomic steps. High Resolution Transmission Electron Microscopy (HRTEM) micrographs of the 40 Å well show a very low interface roughness of 1–2 atomic layers.
Publisher
Springer Science and Business Media LLC
Reference7 articles.
1. Properties of a Si doped GaN/AlGaN single quantum well
2. Fundamental optical transitions in GaN
3. 7. Behr D. , Niebuhr R. , Wagner J. , Bachem K.H. , Kaufmann U. , Appl. Phys. Lett, (to be published)
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献