Nanocrystalline Silicon for Optoelectronic Applications

Abstract

Light emission in silicon has been intensively investigated since the 1950s when crystalline silicon (c-Si) was recognized as the dominant material in microelectronics. Silicon is an indirect-bandgap semiconductor and momentum conservation requires phonon assistance in radiative electron-hole recombination (Figure 1a, top left). Because phonons carry a momentum and an energy, the typical signature of phonon-assisted recombination is several peaks in the photoluminescence (PL) spectra at low temperature. These PL peaks are called “phonon replicas.” High-purity c-Si PL is caused by free-exciton self-annihilation with the exciton binding energy of ~11 meV. The TO-phonon contribution in conservation processes is most significant, and the main PL peak (~1.1 eV) is shifted from the bandgap value (~1.17 eV) by ~70 meV—that is, the exciton binding energy plus TO-phonon energy (Figure 1a).