Rapidly Solidified Binary Tial Alloys

Abstract

AbstractMelt spinning has been carried out on binary TiAl alloys at three Ti/Al ratios. Antiphase domains were observed in one ribbon specimen, but no significant disordering was induced by the rapid solidification as indicated by X-ray and electron diffraction analyses. Bending tests of both the ribbons and the consolidated counterparts showed a decrease in ductility with increasing Al concentration. This compositional effect can be correlated with the TiAl tetragonality (the c/a ratio) as well as the grain structure.