Effect of Interphase Boundary Character on Mechanical Properties in NiAl(β) Bicrystals with Ni 3Al(γ') Precipitates along Grain Boundary

Abstract

ABSTRACTRole of the crystallography of Ni 3Al(γ') precipitates along grain boundaries of NiAl(β) in the mechanical properties was systematically investigated using β bicrystals with controlled orientations. γ' phase preferentially precipitated along βgrain boundaries showing a film-like shape. The selected variant of γ'-film satisfied the Kurdjumov-Sachs (K-S) relation with a neighboring βcrystal but it deviated from the relation with another adjacent βcrystal. In the course of tensile deformation at room temperature, fracture occurred preferentially at incoherent (β/γ') interphase boundary deviating from the K-S relation and the fracture stress decreased with increasing deviation angle. In contrast, the interphase boundary sliding occurred preferentially at irrational (β/γ') interface at 1073K. The sliding displacement increased with increasing deviation angle. Thus, the mechanical properties of β bicrystals with γ'-film were found to depend strongly on the interphase boundary character.