Fukui Toshimi,Sakurai Chihiro,Okuyama Masahiko
Abstract
Ba(Mg1/3Nb2/3)O3 powders were prepared through an alkoxide-hydroxide route. Their sintering behavior and crystallographic structures were investigated, and microwave properties of the obtained ceramics were also measured. Crystalline powder with approximately 0.5 μm in particle size was obtained by the reaction of Ba(OH)2−8H2O and Mg–Nb double alkoxide, Mg[Nb(OEt)6]2, in ethanol-acetone solution. A powder compact sintered at 1350 °C for 2 h showed >99% of relative density and >0.9 of ordering degree of the B site. The Q value of Ba(Mg1/3Nb2/3)O3 ceramics was sensitive to sintering conditions due to the formation of an impurity phase. The ceramics sintered at 1350 °C for 5 h showed a dielectric constant ∊ of 32 and Q value of > 13 000 at 11.8 GHz. The temperature coefficient of resonant frequency τf was 23.9 ppm/°C at 9.8 GHz.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference26 articles.
1. Low-Temperature Route to Lead Magnesium Niobate
2. Microwave Loss Quality of BaZn13Ta2/3O3 Ceramics
3. 8. Hiuga T. , Matsumoto K. , and Ichimura H. , Densi-tsuusin-gakkai, CPM86–31, 41–46 (1986) [in Japanese].
4. Ceramics for microwave dielectric resonator
5. 25. Sugiyama M. , Inuzuka T. , and Kubo H. , in Ceram. Trans., edited by Nair K. M. , Pohanka R. , and Buchanan R. C. , 15 (1990).
Cited by
21 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献