Plastic Deformations in Single Crystals of FePd with the L10 Structure

Abstract

AbstractCompressive deformations of L10-ordered single crystals of FePd have been investigated from room temperature to 873 K. The critical resolved shear stress for superlattice dislocations is hard to determine resulting from buckling that occurs after a small amount of conventional plastic deformation. The CRSS for superlattice dislocations determined from yield stress is significantly larger than that of ordinary dislocations. The CRSS for octahedral glide of ordinary and superlattice dislocations are virtually independent of the temperature, and the positive temperature dependence of the yield stress is not observed for both, ordinary and superlattice dislocations, by the present experiments.