High Efficiency, Large Area, Nanocrystalline Silicon Based, Triple-Junction Solar Cells

Abstract

ABSTRACTWe have fabricated large-area, thin-film multijunction solar cells based on hydrogenated amorphous silicon (a-Si:H) and nanocrystalline silicon (nc-Si:H) made in a large area batch reactor. The device structure consisted of an a-Si:H/nc-Si:H/nc-Si:H stack on Ag/ZnO back reflector coated stainless steel substrate, deposited using our proprietary High Frequency (HF) glow discharge technique. For the nc-Si:H films, we investigated two deposition rate regimes: (i) low rate <1 nm/s and (ii) high rate >1 nm/s. We optimized the deposition parameters, such as pressure, gas flow, dilution, and power. We did SIMS analysis on the optimized films, and found the impurity concentrations were one order of magnitude lower than the films made with the conventional RF process. In particular, the oxygen concentration is reduced to ~1018 cm-3. This value is among the lowest oxygen concentration reported in literature. The low impurity content is attributed to proprietary cathode hardware and the optimized deposition process. During the initial optimization and investigative phase, we fabricated small-area (0.25 cm2 and 1.1 cm2) cells. The information obtained from the initial phase was used to fabricate large-area (aperture area 400 cm2) cells, and encapsulated the cells using the same flexible encapsulants that are used in our commercial product. We have light soaked the low-rate and high-rate encapsulated modules. The highest initial efficiency of the low-rate modules is 12.0% as confirmed by NREL. The highest corresponding stable efficiency attained for the low-rate samples cells is 11.35%. For the high-rate small-area (1.1 cm2) cells, the highest initial active-area efficiency and corresponding stable efficiency attained are 13.97% and 12.9%, respectively. We present the details of the research conducted to develop the low- and high-rate cells and modules.