The Effect of Fine M2C (M: Mo, Cr, Fe) Particles on the Recrystallization Temperature and High Temperature Strength of Warm Rolled Fe3Al Based Alloys

Abstract

ABSTRACTThe effect of fine M2C particles on the recrystallization temperature and high temperature strength of warm rolled Fe3Al base alloys was investigated. Fe-27Al-1.2C-2Cr-xMo (x: 0.3, 0.9) alloys (in at.%) were arc melted, warm rolled and annealed. TEM observations have revealed that fine M2C particles were present in the alloy containing 0.9% Mo but not in the alloy with 0.3% Mo after warm rolling. The recrystallization temperature increased from 740 °C to 810 °C when the Mo content is increased from 0.3 to 0.9 due to the presence of fine M2C particles. Tensile tests conducted on annealed samples with fine sub-grained matrix have shown that the introduction of fine M2C particles is effective to enhance the proof stress at 600 °C.