Author:
Foltyn S. R.,Peterson E. J.,Coulter J. Y.,Arendt P. N.,Jia Q. X.,Dowden P. C.,Maley M. P.,Wu X. D.,Peterson D. E.
Abstract
To investigate potential limits to the rate at which high-quality YBa2Cu3O7–δ can be deposited, we have produced a series of 1 μm thick films by pulsed laser deposition on single-crystal SrTiO3 substrates at average rates ranging from 2 Å/s to 240 Å/s. The critical current density of low-rate films was over 2 MA/cm2 at 75 K, self field, but dropped linearly with rate to about 1 MA/cm2 at the upper end of the range. In addition, the superconducting transition temperature, resistivity above the transition, and performance in an applied magnetic field were all degraded by increasing the deposition rate. A change in c-axis lattice parameter suggests that possible causes for this degradation are oxygen deficiency or cation disorder with the latter being the more likely. Annealing high-rate films at 790 °C for as little as 20 min improved critical current density to within 20% of low-rate values, and resulted in dramatic improvements in other film properties as well.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Cited by
56 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献