Irradiation Effects in the Storage and Disposal of Radioactive Ion-Exchange Resins

Abstract

ABSTRACTResearch is under way to characterize the effects of self-irradiation on radwastes which may be generated when organic ion-exchange media are used in water demineralization or decontamination operations at nuclear facilities. External factors affecting the relation between laboratory evaluations and field performance are emphasized. Initial experiments do not yet indicate substantial radiation dose-rate effects on radiolytic gas yields or acid product formation, when (fully swollen) sulfonic acid resins are irradiated in a sealed air environment. At the same time, oxygen gas is removed from the environment of irradiated resins. Interaction between mild steel coupons and acidic species produced in the irradiation induced decomposition of sulfonic acid resin results in irradiation enhanced corrosion. Corrosion rates depend on radiation dose rate, moisture content and resin chemical loading. In some cases, corrosion rates decrease with time, suggesting depletion of acidic species within the resin bed, or a synergistic interaction between resin and corrosion coupon. Implications of these and other results on evaluating field behavior of radwaste containing ion-exchange media are discussed.