Author:
Field R. D.,Krueger D. D.,Huang S. C.
Abstract
ABSTRACTRoom temperature tensile tests were performed on annealed melt-spun ribbons of a 50Ni-20Al-30Fe alloy. The ribbons were found to possess a duplex structure consisting of fcc γ and B2 β grains and exhibited tensile elongations in excess of 10% while still maintaining good strength. The tested specimens were found to contain high dislocation densities in both the γ and β grains, with no indications of stress-induced martensite formation. Dislocation analysis revealed that the vast majority of dislocations in the β have <100> Burgers vectors; however, <111> dislocations were also observed. Slip transfer was often facilitated by specific orientation relationships between the γ and β grains.
Publisher
Springer Science and Business Media LLC
Reference21 articles.
1. Anomalies in the electron diffraction patterns of nickel-rich β′-NiAl alloys
2. 10) Taub A , Palmer C P , Chang K M , and Huang S C , in Mechanical Behavior of Rapidly Solidified Materials, Proceedings: AIME Annual Meeting, Feb. 1985.
3. Ductility in rapidly solidified NiAl
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献