The influence of mill energy and temperature on the structure of the TiNi intermetallic after mechanical attrition

Author:

Yamada Kenjiro,Koch Carl C.

Abstract

Mechanical attrition of intermetallic compound TiNi powder was carried out in two different ball mills and as a function of milling temperature. The microstructural changes with milling time were followed by x-ray diffraction, TEM, and DSC. The more energetic Spex shaker mill provided a higher degree of lattice strain and rapidly refined the grain size to the nanometer size regime. Amorphization was observed in the Spex mill with a linear increase in the milling time for amorphization with increasing milling temperature. No amorphization was observed in the less energetic vibratory mill, and the grain size saturated to a constant value of 15 nm after ≥60 h of milling. A critical grain size for the amorphization of 4–5 nm was estimated from the temperature dependent studies in the Spex mill. The grain boundary energy (706 mJ/m2), estimated from the vibratory mill experiments, and the above critical grain sizes (5 nm) for amorphization were used to calculate the enthalpy supplied by the nanocrystalline grain boundaries. The calculated value of 4.1 kJ/mol was comparable to the measured enthalpy of crystallization of 3.2 kJ/mol. It is concluded that the nanocrystalline grain boundary energy is responsible for driving the crystalline-to-amorphous phase transformation induced by mechanical attrition in TiNi.

Publisher

Springer Science and Business Media LLC

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

Cited by 70 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3