Author:
Silverman L. A.,Teowee G.,Uhlmann D. R.
Abstract
ABSTRACTWe have studied the densification and dielectric properties of sol-gel derived tantalum oxide thin films as the insulators in MIS capacitors. Hydrolysis of tantalum ethoxide is extremely rapid and goes to completion in ethanol. Condensation is also rapid, and goes to completion in toluene Multiple layers were applied by spin-coating up to thicknesses of 3000 Å before cracking of the coating during drying ensued. Densification occurs from room temperature to 450 C, with the original film thickness decreasing by about half in one hour at 450 C. No additional densification occurs upon heating to 750 C. The dielectric constant decreases from unfired samples to those fired at 450 C, and then increases on firing from 600 to 750 C. The value of the dielectric constant at 1 MHz for samples fired at 750 C for one hour is 20, similar to that of anodically grown Ta2O5. Leakage currents as low as 2 × 10−7 amp cm−2 have been measured for applied fields of 200,000 V cm−1.
Publisher
Springer Science and Business Media LLC
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献