Author:
Grun J.,Manka C.K.,Hoffman C. A.,Meyer J. R.,Glembocki O. J.,Qadri S. B.,Skelton E. F.,Donnelly D.,Covington B.
Abstract
AbstractWe experimentally demonstrate the annealing and electrical activation of doped silicon without the direct application of heat as in conventional thermal annealing or pulsed laser annealing. 25 × 25 × 3 mm samples of silicon doped by neutron transmutation were irradiated with a short pulse from a 1.06-micron laser. The few joule laser pulse was focused to mm-diameter surface spot which resulted in high power (∼ 1011W/cm2) capable of launching shocks into the entire sample. In a few instances the entire silicon slab, including regionsfar outside the illuminated spot, was annealed and electrically activated. In the annealed samples electrical activation of donors throughout the slab, measured with a four-point probe, was uniform and comparable to that of thermally annealed control samples. Far-infrared spectroscopy and Hall measurements also showed that the donor species was activated and Raman spectroscopy demonstrated marked improvement in the crystal structure. We conjecture that the annealing was caused by the mechanical energy that was launched into the slab by the laser pulse. Results of experiments on an ion-implanted silicon sample are also discussed.
Publisher
Springer Science and Business Media LLC
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献