Growth and Characterization of Na0.5K0.5NbO3 Thin Films on Polycrystalline Pt80Ir20 Substrates

Abstract

Na0.5K0.5NbO3 thin films have been deposited onto textured polycrystalline Pt80Ir20 substrates using radio frequency magnetron sputtering. Films were grown in off- and on-axis positions relative to the target at growth temperatures of 500–700 °C and sputtering pressures of 1–7 Pa. The deposited films were found to be textured, displaying a mixture of two orientations (001) and (101). Films grown on-axis showed a prefered (001) orientation, while the off-axis films had a (101) orientation. Scanning electron microscopy showed that the morphology of the films was dependent on the substrate position and sputtering pressure. The low-frequency (10 kHz) dielectric constants of the films were found to be in the range of approximately 490–590. Hydrostatic piezoelectric measurements showed that the films were piezoelectric in the as-deposited form with a constant up to 14.5 pC/N.