Author:
Marucco J. F.,Noguera C.,Garoche P.,Collin G.
Abstract
The YBa2Cu3Oz system has been investigated by thermogravimetry in a controlled partial oxygen pressure PO2 ranging from 105-10 Pa. A compound with z = 6.290 was prepared at T = 950°C and PO2 = 105 Pa and identified as a metastable β phase. Subsequent isothermal or isobar phase stability studies were performed. This β phase has a narrow metastability domain 6.25 <z < 6.50 at high temperature. By decreasing the temperature or increasing the PO2, the β phase transforms irreversibly into an α phase characterized by large deviations 7—x from stoichiometry. Near the stoichiometry z = 7, the structure of the a phase is orthorhombic, and fully ionized vacancies are likely to be predominant. By decreasing the PO2, the β phase transforms into a new phase with a lower oxygen content (z < 6.1).
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference7 articles.
1. Effect of Oxygen Deficiency on the Crystal Structure and Superconducting Properties of the Ba2YCu3Oy
2. Contribution à l'étude thermodynamique des oxydes de tungstène, à 1 000 °C, dans le domaine [math]
3. The Chemistry of Imperfect Crystals
4. Mixed-valence copper oxides can be used as electrodes for capacitors
5. 2 Schuller I. K. , Hinks D. G. , Beno M. A. , Capone D. W. II , holm L. Soder- , Locquet J. P. , Brugnceraede Y. , Segre C. U. , and Zhang K. , Solid State Commun. (to be published).
Cited by
22 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献