YBa2Cu3O7−x Grain Boundary Weak Links on MgO Bicrystal

Abstract

ABSTRACTThe characteristics of YBa2Cu3O7−x (YBCO) thin films by laser ablation on MgO bicrystals have been investigated. The bicrystals were fabricated by hot pressing two single crystals with the configuration of [001] tilt boundaries. The YBCO films were epitaxial grown with C-axis normal to the both adjacent grains of bicrystals. The FWHM about (005) reflection was 0.4–0.5 degree, indicating the high degree of the oriention for the film with small mosaic spread. Our preliminary study showed that the typical value of Jc on either side of the bicrystal boundary was 0.4–10×106 A/cm2 at 15K, while that across the 10° tilt boundaries was 0.3–9×105 A/cm2 at 15K. These results implied that the artificial grain boundaries effectively weakened the supercurrent, and therefore, the weak-link properties of artificial boundaries were more easily controllable than those of naturally occuring grain boundaries.