On the Effect of Local Grain-Boundary Chemistry on the Macroscopic Mechanical Properties of a High Purity Y2O3-Al2O3-Containing Silicon Nitride Ceramic

Abstract

ABSTRACTThe effects of grain-boundary chemistry on the mechanical properties of a high-purity silicon nitride ceramics were investigated, with specific emphasis on the role of oxygen. Variations in the grain-boundary oxygen content, through control of oxidizing heat treatments and sintering additives, was found to result in a transition in fracture mechanism from transgranular to intergranular fracture, with an associated increase in fracture toughness. This phenomenon is correlated to an oxygen-induced change in grain-boundary chemistry that appears to affect fracture by “weakening” the interface, facilitating debonding and crack advance along the boundaries, thereby enhancing the toughness by grain bridging. It is concluded that if the oxygen content in the thin grain-boundary films exceeds a lower limit, which is ∼0.87 equiv% oxygen content, then the interfacial structure and bonding characteristics favor intergranular debonding during crack propagation; otherwise, transgranular fracture ensues, with consequent low toughness.