Huang M. L.,Wang L.,Wu C. M. L.
Abstract
Precipitation-strengthened tin-based eutectic Sn–3.5 Ag alloy was investigated for its creep behavior at three temperatures ranging from 303 to 393 K, under the tensile stress range of σ/E = 10−4 to 10−3. The steady-state creep rates cover seven orders of magnitude (10−3 to 10−9 s−1). The initial microstructure was found to have Ag3Sn intermetallic compound finely dispersed in the matrix of β–Sn. By incorporation of a threshold stress, σth, into the analysis, the creep data of eutectic Sn–Ag at all temperatures can be fitted by a single straight line with a slope of seven after normalizing the steady-state creep rate and the effective stress, indicating that the creep rates are controlled by the dislocation-pipe diffusion in the Sn matrix. The steady-state creep rate, , can then be expressed as , where QC is the creep activation energy, G is the temperature-dependent shear modulus, b is Burger's vector, R is the universal gas constant, T is the absolute temperature, σ is the applied stress, A is a material-dependent constant, and , in which σOB is the Orowan bowing stress and kR is the relaxation factor.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Cited by
83 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献