Bloyer D. R.,Rao K. T. Venkateswara,Ritchie R. O.
Abstract
AbstractA brittle intermetallic, Nb3Al, reinforced with a ductile metal, Nb, has been used to investigate the resistance curve and cyclic fatigue behavior of a relatively coarse laminated composite. With this system, the toughness of Nb3Al was found to increase from ∼1 MPa√m to well over 20 MPa√m after several millimeters of stable crack growth; this was attributed to extensive crack bridging and plastic deformation within the Nb layers in the crack wake. Cyclic fatigue-crack growth resistance was also improved in the laminate microstructures compared to pure Nb3Al and Nb-particulate reinforced Nb3Al composites with crack arrester orientations in the laminate providing better fatigue resistance than either the matrix or pure Nb.