Durabilities and Microstructures of Radioactive Glasses for Immobilization of Excess Actinides at the Savannah River Site

Author:

Bibler N. E.,Ramsey W. G.,Meaker T. F.,Pareizs J. M.

Abstract

AbstractThis paper presents results of an investigation of the microstructures and durabilities of glasses for immobilization of excess Pu, Am, and Cm at the Savannah River Site (SRS). The glasses investigated had compositions based on commercial lanthanide glasses developed in the 1930's. All the glasses were prepared remotely in shielded cells and the analyses performed using instruments in radio hoods or benches. Durabilities were measured using the ASTM C-1285 standard leach test (PCT). Results for three glasses are presented. Two glasses contained 15 and 7 wt.% Pu, respectively. The third glass contained Am and Cm. The 15 wt% Pu glass was not completely amorphous and contained crystals of undissolved PuO2 and as well as dissolved PuO2. The 7 wt% Pu glass was completely amorphous. The Am/Cm glass contained <1 wt% actinides and was homogenous. The PCT tests for the Pu glasses indicated that B and Ba were leached congruently. Sm and Pu were leached at slower rates. In some cases release rates for specific Ba, Sm, and Pu isotopes were measured by analyzing the leachates by mass spectroscopy. For the Am-Cm glass release rates for B and Ba were equal indicating congruent dissolution. All three glasses were 25 to 50 times more durable than the borosilicate glasses developed at SRS for immobilization of the fission product HLW resulting from reprocessing operations at SRS.

Publisher

Springer Science and Business Media LLC

Subject

General Engineering

Cited by 18 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3