Lange F. F.,Falk L. K. L.,Davis B. I.
Abstract
An investigation was made of the effect of Y2O3 in solid solution in ZrO2 on the phases that are formed when ZrO2 is reacted with either N2 or Si3N4. The results suggest that the Zr–oxynitride phase can be predcluded as a reaction product when the Y2O3 content of the ZrO2 is ≥4 mol %. Dense Si3N4/ZrO2(+ Y2O3) composites were fabricated, which did not degrade during oxidation at temperatures %le; 1000°C. Severe degradation was observed for composites containing the Zr-oxynitride phase. The fracture toughness of the Si3N4/ZrO2(+ Y2O3) composites increased with ZrO2 content.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference26 articles.
1. 2 Vasilos T. , Cannon R. M. Jr. , and Wuensch B. J. , Final National Aeronautics and Space Administration Report No. NASA-CR-159585, 30 March 1979.
2. Transformation toughening
3. Electron microscopy investigation of the ZrO2-ZrN system—I. Formation of an incommensurate superstructure ZrON
Cited by
49 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献