Translucency and Wear of Pressable Lithium Disilicate and Zirconia-reinforced Lithium Silicate Glass-ceramics: An In-vitro Study

Author:

Potdukhe Shruti S,Iyer Janani M,Nadgere Jyoti B

Abstract

Introduction: New ceramic materials have been introduced with less research on their aesthetic outcome and durability for clinical implications. Lithium disilicate is one of the widely used materials for restoration. Recently, Zirconia-reinforced Lithium Silicate (ZLS) glass-ceramic enriched with 10% zirconia in highly dispersed glass phase of ceramic has been introduced. Aim: To investigate the translucency of pressable Lithium Disilicate (LS2 ) and ZLS and their effects on wear of opposing enamel. Materials and Methods: This in-vitro study was carried out at MGM Dental College and Hospital, Mumbai, Maharashtra, India, between January 2017 and January 2020. Twenty disks of 15×3 mm; 10 each of LS2 and ZLS were fabricated by hot pressing method. For translucency Commission Internationale de l’Eclairage (CIE) L*a*b values for each sample were measured against black and white background using a laboratory reflectance spectrophotometer. Translucency was calculated using Translucency Parameter (TP)= {(L*B-L*W)2 +(a*Ba*W)2 +(b*B-b*W)2 }1/2. For wear testing same 20 disks were used as an antagonist. Enamel specimen of 20 maxillary premolar were abraded against each antagonist with two body wear testing machine in rotational motion under a constant load of 20 N at 350 rpm for 5000 cycles. The initial readings and final readings of enamel specimen in μm were measured using contact stylus profilometer. Non parametric Mann-Whitney U test was used to compare the significance of difference between two groups. Results: The TP values obtained were 23.07 and 24.04 for LS2 and ZLS, respectively (p-value=0.004). The mean wear values obtained were 0.71860 μm and 1.09500 μm for LS2 and ZLS, respectively (p-value=0.049). The difference for both the parameters was statistically significant. Conclusion: Within the limitation of this study, ZLS showed higher translucency values than LS2 . Wear rate of opposing enamel was more with ZLS than LS2 . Thus ZLS may provide excellent aesthetics which can be used as an option for rehabilitation in aesthetic zone.

Publisher

JCDR Research and Publications

Subject

Clinical Biochemistry,General Medicine

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3