The possibility of the application of impact microindentation method for testing the physic and mechanical properties of cast iron using the IFMH-C instrument developed at the Institute of applied physics of the National Academy of Sciences of Belarus was tested. It was established that the method and the instrument allow to estimate such parameters as Brinell hardness in the range of 100–500 HB, elastic modulus from 40 to 200 MPa, as well as to determine the tensile strength of the flake and spheroidal graphite cast irons. The possibility of using the instrument for non-destructive test directly of parts and products in the manufacturing environments is shown.
Publisher
Belarusian National Technical University
Subject
Pulmonary and Respiratory Medicine,Pediatrics, Perinatology, and Child Health
Reference7 articles.
1. Maki S., Yamamoto T. Computer Simulation of Micro Rebound Hardness Test // Procedia Engineering, 2014, vol. 81, pp. 1396–1401.
2. Sherman A. D. Chugun: Spravochnik [Cast iron: Handbook]. Moscow, Metallurgija Publ, 1991. 576 p.
3. Orłowicz W., Tupaj M., Mróz M., Guzik E. Evaluation of ductile iron casting material quality using ultrasonic testing. Journal of Materials Processing Technology, 2010, vol. 210, no 11, pp. 1493–1500.
4. Majorov A. L., Bajev A. R., Konovalov G. E., Gil N. N. The results of using of indicators of the high-test cast iron of type ICH structure in conditions of production. Lit’e i metallurgiya = Foundry production and metallurgy, 2006, no. 2, vol. 1, pp. 102–105 (in Russian).
5. Rudnitsky V. A., Kren A. P., Lantsman G. A. Evaluation of metallic materials plasticity by dynamic indentation method. Lit’e i metallurgiya = Foundry production and metallurgy, 2017, no. 2, pp. 81–87 (in Russian).