Effect of CNT-Based Resin Modification on the Mechanical Properties of Polymer Composites

Author:

Nayak Suhas Yeshwant,Shenoy Satish,Hameed Sultan Mohamed Thariq,Kini Chandrakant R.,Seth Aashna,Prabhu Shrinivasa,Safri Syafiqah Nur Azrie

Abstract

In this study an attempt was made to explore the possibility of substituting 3D E-glass fabric with eco-friendly basalt fabric along with the modification of resin using MWCNTs, a material system about which very limited information exists. The study involved comparing the mechanical properties of two sets of composites. The first set was comprised of 3D orthogonally woven E-glass-reinforced epoxy composites, basalt-reinforced epoxy composites, and hybrid 3D E-glass orthogonally woven/basalt-reinforced epoxy composites while the second set of composites was the same as the first but prepared with resin modified with Multi Walled Carbon Nanotubes (MWCNTs). All the composites were fabricated by hand lay-up and compression molding techniques. To modify the resin for the second set of composites, MWCNTs were dispersed into the epoxy resin with acetone as a surfactant by magnetic stirring and ultra-sonification. Mechanical tests included tensile, flexural, and low velocity impact strength which were evaluated as per standards. Scanning electron microscopy (SEM) was employed to study the fractured surfaces. Results showed that resin modification did not yield any positive results on the mechanical properties of the composites. The highest tensile (364.4 MPa) and flexural strength (345.3 MPa) was obtained for 3D E-glass composites followed by basalt composites and hybrid 3D E-glass/basalt composites while the highest impact strength of 198.42 kJ/m2 was exhibited by the hybrid 3D E-glass/basalt composites. SEM micrographs showed de-bonding between the modified matrix and fiber which was seen as one of the primary causes for relatively poor performance of the composites prepared with modified resin. Fiber breakage, matrix cracking, fiber pull-out, and delamination were the other modes of failure. Results suggest that hybridization with basalt fibers is a much safer, more cost effective, and eco-friendly option over resin modification.

Funder

Universiti Putra Malaysia

Publisher

Frontiers Media SA

Subject

Materials Science (miscellaneous)

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3