Peeling Force Required for the Detachment of Non-Woven Plastic Tissue from the Surface of Mortar Prisms

Abstract

The purpose of this experimental paper is to examine the adhesion properties between non-woven plastic sheets and cement mortar. Specifically, the effect of w/c ratio and quantity of superplasticizer on the peeling force required for the detachment of tissue from the surface of prisms was studied in detail. Therefore, two types of mortar mixtures were prepared: (1) mixtures without superplasticizer with three different w/c ratios of 0.45, 0.50, and 0.55, and (2) mixtures with reduced amounts of water and three various percentages of superplasticizer of 0.0%, 1.11%, and 2.17% (by weight of cement). For this purpose, bond tests with a special setup, interferometry and microscopic analyses, and mechanical tests were performed. The results highlight that non-woven sheets had strong adhesion to cement mortar without using any adhesive materials. However, the peeling force improved by 15.78% as the w/c ratio increased from 0.50 to 0.55. Conversely, this force declined by 24.50% as the w/c ratio decreased from 0.50 to 0.45. In addition, the peeling force decreased by 20.62% as the w/c ratio decreased from 0.50 to 0.45 and 1.11% superplasticizer was added to the mixtures. This property decreased further by 38.29% as the w/c ratio lowered to 0.40, and the amount of superplasticizer increased to 2.17%. The interferometry and microscopic analyses clearly demonstrate that the adhesion between tissue and mortar is largely related to the surface texture, amount of cement paste, and quantity of residual fibers on the surfaces of samples. It indicates that mortar samples with higher w/c ratios had a smoother surface, and providing more contact area for microfilaments, which resulted in thicker layers of remaining fibers compared to the specimens with a lower w/c ratio. Even though there was not much difference in the surface texture of specimens with superplasticizer and lower w/c ratios, because of their similar workability. Still, thicker layers of microfilaments remained on the surface of specimens containing a lower amount of superplasticizer, which resulted in strong adhesion between sheet and cement mortar.