Synthesis and Characterization of Cardanol-Based Non-Isocyanate Polyurethane
Author:
Li Yanan1, Zhang Bin1, Zhao Yuzhuo1, Lu Shuai1, Fan Donglei1, Wang Song1, Liu Jie2, Tang Tao2, Li Sanxi1
Affiliation:
1. School of Environmental and Chemical Engineering, Shenyang University of Technology, Shenyang 110870, China 2. State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
Abstract
This paper describes the synthesis of NIPU by using cardanol as starting material. A cardanol formaldehyde oligomer was first prepared through the reaction of cardanol and formaldehyde, catalyzed by citric acid. The resulting oligomer was then subjected to epoxidation with m-chloroperbenzoic acid to obtain an epoxide compound, which was subsequently used to fix carbon dioxide (CO2) and form a cyclic carbonate. Using this cyclic carbonate, along with an amine, cardanol-based isocyanate polyurethane (NIPU) was prepared. Different characterization methods, such as Fourier transform infrared spectroscopy (FTIR), proton nuclear magnetic resonance (NMR), gel permeation chromatography (GPC), and thermogravimetric analysis (TGA), were used to confirm the synthesis of the four intermediate products and NIPU in the reaction process. This study highlights the promise of bio-based NIPU as a sustainable alternative in a number of applications while offering insightful information on the synthesis and characterization of the material.
Funder
National Natural Science Foundation of China Key Laboratory of Polymer and Catalyst Synthesis Technology of Liaoning Province Discipline Team Building Program of Shenyang University of Technology
Subject
Polymers and Plastics,General Chemistry
Reference40 articles.
1. Non-Isocyanate Polyurethane/Epoxy Hybrid Materials with Different and Controlled Architectures Prepared from a CO2-Sourced Monomer and Epoxy via an Environmentally-Friendly Route;Ke;RSC Adv.,2017 2. Aristri, M.A., Lubis, M.A.R., Yadav, S.M., Antov, P., Papadopoulos, A.N., Pizzi, A., Fatriasari, W., Ismayati, M., and Iswanto, A.H. (2021). Recent Developments in Lignin- and Tannin-Based Non-Isocyanate Polyurethane Resins for Wood Adhesives—A Review. Appl. Sci., 11. 3. El Khezraji, S., Chaib, M., Thakur, S., Raihane, M., Lopez-Manchado, M.A., Verdejo, R., and Lahcini, M. (2022). Synthesis of Novel Non-Isocyanate Polyurethane/Functionalized Boron Nitride Composites. Polymers, 14. 4. Stachak, P., Łukaszewska, I., Hebda, E., and Pielichowski, K. (2021). Recent Advances in Fabrication of Non-Isocyanate Polyurethane-Based Composite Materials. Materials, 14. 5. Smith, D.L., Rodriguez-Melendez, D., Cotton, S.M., Quan, Y., Wang, Q., and Grunlan, J.C. (2022). Non-Isocyanate Polyurethane Bio-Foam with Inherent Heat and Fire Resistance. Polymers, 14.
|
|