Filament Extrusion and Its 3D Printing of Poly(Lactic Acid)/Poly(Styrene-co-Methyl Methacrylate) Blends

Abstract

Herein, we report the melt blending of amorphous poly(lactide acid) (PLA) with poly(styrene-co-methyl methacrylate) (poly(S-co-MMA)). The PLAx/poly(S-co-MMA)y blends were made using amorphous PLA compositions from 50, 75, and 90wt.%, namely PLA50/poly(S-co-MMA)50, PLA75/poly(S-co-MMA)25, and PLA90/poly(S-co-MMA)10, respectively. The PLAx/poly(S-co-MMA)y blend pellets were extruded into filaments through a prototype extruder at 195 °C. The 3D printing was done via fused deposition modeling (FDM) at the same temperature and a 40 mm/s feed rate. Furthermore, thermogravimetric curves of the PLAx/poly(S-co-MMA)y blends showed slight thermal decomposition with less than 0.2% mass loss during filament extrusion and 3D printing. However, the thermal decomposition of the blends is lower when compared to amorphous PLA and poly(S-co-MMA). On the contrary, the PLAx/poly(S-co-MMA)y blend has a higher Young’s modulus (E) than amorphous PLA, and is closer to poly(S-co-MMA), in particular, PLA90/poly(S-co-MMA)10. The PLAx/poly(S-co-MMA)y blends proved improved properties concerning amorphous PLA through mechanical and rheological characterization.