Synthesis, Characterization and Catalytic Evaluation of Chromium Oxide Deposited on Titania–Silica Mesoporous Nanocomposite for the Ethane Dehydrogenation with CO2

Abstract

Ti modification of mesoporous silica support has been reported as an effective way to enhance Cr–Ti–Si interactions that, in turn, impact the catalytic dehydrogenation of ethane with CO2. However, such modification necessitates a repeated, time-consuming and tedious process. In this work, a simple, fast and facile approach has been utilized to synthesize chromium-oxide-loaded titania–silica mesoporous nanocomposites. A series of Cr(y)/Ti(x)–Si mesoporous nanocomposite catalysts with varying Ti and Cr contents were prepared and tested in the dehydrogenation of ethane with carbon dioxide. The as-synthesized catalysts were characterized by XRD, TEM, SEM, BET, UV–Vis–DR, XPS and H2–TPR techniques. The effect of titanium content, as well as chromium loading on the performance of the prepared Cr(y)/Ti(x)–Si catalysts, was investigated. It was found that 2.2 and 8 wt % are the optimum titanium and chromium contents in the synthesized catalysts for obtaining the highest catalytic activity. The superior catalytic performance of the Cr(8)/Ti(2.2)–Si catalyst can be attributed to a higher dispersion of the Cr species, as well as a higher content of the redox Cr species on the surface of the Cr/Ti–Si catalyst. The results showed that the Cr(8)/Ti(2.2)–Si catalyst efficiently dehydrogenated C2H6 in the presence of CO2 giving a 52.3% ethane conversion and 48.0% ethylene yield at 700 °C reaction temperature.