Abstract
The crack propagation mechanism of Cu nanowires is investigated by using molecular dynamics methods. The microstructural evolution of crack propagation at different strain rates and crack depths is analyzed. Meanwhile, the stress intensity factor at the crack tip during crack propagation is calculated to describe the crack propagation process of Cu nanowires under each condition. The simulation results show that the competition between lattice recovery and dislocation multiplication determines the crack propagation mode. Lattice recovery dominates the plastic deformation of Cu nanowires at low strain rates, and the crack propagation mode is shear fracture. With the increase in strain rate, the plastic deformation mechanism gradually changes from lattice recovery to dislocation multiplication, which makes the crack propagation change from shear fracture to ductile fracture. Interestingly, the crack propagation mechanism varies with crack depth. The deeper the preset crack of Cu nanowires, the weaker the deformation resistance, and the more likely the crack propagation is accompanied.
Funder
National Natural Science Foundation of China
Subject
General Materials Science,General Chemical Engineering
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献