Abstract
In this paper, the influence of the Fe2O3 addition amount on the dephosphorization of hot metal at 1623 K with the slag of the low basicity (CaO/SiO2) of about 1.5 was investigated by using high-temperature laboratorial experiments. With increasing the Fe2O3 addition amount from 5 to 30 g, the contents of [C], [Si], [Mn] and [P] in the hot metal at the end of dephosphorization are decreased and the corresponding removal ratios increase. In dephosphorization slags, the phosphorus mainly exists in the form of the nCa2SiO4–Ca3(PO4)2 solid solution in the phosphorus-rich phase and the value of coefficient n decreases from 20 to 1. Furthermore, the oxygen potential and activity at the interface between the slag and hot metal are increased. When the oxygen potential and the oxygen activity at the interface are greater than 0.72 × 10−12 and 7.1 × 10−3, respectively, the dephosphorization ratio begins to increase rapidly. When the Fe2O3 addition amount is increased to 30 g, the ratio of the Fe2O3 addition amount to theoretical calculation consumption is around 175%, and the dephosphorization ratio reaches the highest value of 83.3%.
Funder
National Natural Science Foundation of China
Subject
General Materials Science,Metals and Alloys
Cited by
13 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献