The paper presents results of studies on the impact of bismuth and tin additions to the Zn-AlNi bath on microstructure and corrosion resistance of hot dip galvanizig coatings. The structure at high magnifications on the top surface and cross-section of coatings received in the Zn-AlNiBiSn bath was revealed and the microanalysis EDS (energy dispersion spectroscopy) of chemical composition was determined. The corrosion resistance of the coatings was tested relatively in a neutral salt spray test (NSS), and tests in a humid atmosphere containing SO2. Electrochemical parameters of coatings corrosion were determined. It was found that Zn-AlNiBiSn coatings show lower corrosion resistance in comparison with the coatings received in the Zn-AlNi bath without Sn and Bi alloying additions. Structural research has shown the existence of precipitations of Sn-Bi alloy in the coating. It was found that Sn-Bi precipitations have more electropositive potential in relation to zinc, which promotes the formation of additional corrosion cells.
Subject
General Materials Science
Reference50 articles.
1. Hot-Dip Galvanizing of Steel Structures;Kuklik,2016
2. Zanurzeniowe powłoki aluminiowe na stali zbrojeniowej B500SP
3. The Influence of the Angle of Working Part of Die on the Zinc Coating Thickness and Mechanical Properties of Medium Carbon Steel Wires
4. Continuous Hot-Dip Galvanizing—Process and Products. Galvinfo Center—A Program of the International Zinc Association, Galvanizing-2015;Dallin,2015
5. Antykorozyjne Metalowe Powłoki Zanurzeniowe;Liberski,2013
Cited by
9 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献