Abstract
The temperature and material flow gradients along the thick section of the weld seriously affect the welding efficiency of friction stir welding in medium-thick plates. Here, the effects of different gradients obtained by the two pins on the weld formation, microstructure, and mechanical properties were compared. The results indicated that the large-tip pin increases heat input and material flow at the bottom, reducing the gradient along the thickness. The large-tip pin increases the welding speed of defect-free joints from 100 mm/min to 500 mm/min compared to the small-tip pin. The ultimate tensile strength and elongation of the joint reached 247 MPa and 8.7%, equal to 80% and 65% of the base metal, respectively. Therefore, reducing the temperature and material flow gradients along the thickness by designing the pin structure is proved to be the key to improving the welding efficiency for thick plates.
Funder
National Natural Science Foundation of China
China National Postdoctoral Program for Innovative Talents
Subject
General Materials Science
Cited by
14 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献