Functionally graded tungsten/steel composites are attractive to be used as an interlayer to join tungsten (W) and steel for the first wall of future fusion reactor to reduce the thermally induced stresses arising from the different coefficient of thermal expansion (CTE) of W and steel. W/steel composites, with three W contents: 25, 50 and 75 vol% W, will serve as individual sublayers of this functionally graded material. Therefore, the present work exploits an emerging sintering technique, field-assisted sintering technology, to produce these composites. Firstly, a systematic parameter study was conducted aiming to reduce the residual porosity to a minimum while keeping the formation of intermetallic phases at the W/steel interface at a low level. The optimized composites 25, 50 and 75 vol% W achieved a relative density of 99%, 99% and 96%, respectively. Secondly, mechanical tests at elevated temperatures reveal that these composites are ductile above 300 °C, which is the minimum operating temperature of the first wall. Lastly, the measured CTE, specific heat capacity and thermal conductivity were consistent with the theoretically expected values.
Funder
EUROfusion Consortium, funded by the European Union via the Euratom Research and Training Programme
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献