Abstract
We reported that highly (111)-oriented nanotwinned gold can be fabricated by periodical-reverse electroplating. The as-deposited films are shown to have a strong (111) preferred orientation, increasing with the reverse current time. The ratios of I(111)/I(220) and I(111)/I(200) in X-ray diffraction signals indicates a strong (111) preferred orientation. Using the advantage of the fast surface diffusion of (111) plane compared to the other planes of gold, we performed direct bonding with different thicknesses. Grain growth was observed over two films’ interfaces to eliminate the bonding interface, when annealed at 250 °C for 1 h. Shear tests were performed to gain insight on the bonding quality. All the chips failed at either the silicon substrate or substrate-adhesion layer, showing possible higher strength than the tested maximum, 40.8 MPa.
Funder
Ministry of Science and Technology, Taiwan
Subject
General Materials Science
Reference26 articles.
1. Cramming more components onto integrated circuits, Reprinted from Electronics, volume 38, number 8, April 19, 1965, pp.114 ff.
2. Growth competition between layer-type and porous-type Cu 3 Sn in microbumps
3. Latest Metal Technologies for 3D Integration and MEMS Wafer Level Bondinghttp://www.electron-mec.com/wp-content/uploads/Devices/WP_MEMS_MetalTechnologiesfor3DIntegrationandMEMSWaferLevelBonding_0812.pdf
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献