Abstract
With the intensification of the energy crisis, it is urgent to vigorously develop new environment-friendly energy storage materials. In this work, coexisting ferroelectric and relaxor-ferroelectric phases at a nanoscale were constructed in Sr(Zn1/3Nb2/3)O3 (SZN)-modified (Bi0.5Na0.5)0.94Ba0.06TiO3 (BNBT) ceramics, simultaneously contributing to large polarization and breakdown electric field and giving rise to a superior energy storage performance. Herein, a high recoverable energy density (Wrec) of 5.0 J/cm3 with a conversion efficiency of 82% at 370 kV/cm, a practical discharged energy density (Wd) of 1.74 J/cm3 at 230 kV/cm, a large power density (PD) of 157.84 MW/cm3, and an ultrafast discharge speed (t0.9) of 40 ns were achieved in the 0.85BNBT-0.15SZN ceramics characterized by the coexistence of a rhombohedral-tetragonal phase (ferroelectric state) and a pseudo-cubic phase (relaxor-ferroelectric state). Furthermore, the 0.85BNBT-0.15SZN ceramics also exhibited excellent temperature stability (25–120 °C) and cycling stability (104 cycles) of their energy storage properties. These results demonstrate the great application potential of 0.85BNBT-0.15SZN ceramics in capacitive pulse energy storage devices.
Funder
National Natural Science Foundation of China
Natural Science Foundation of Shandong Province of China
Innovation Team of Higher Educational Science and Technology Program in Shandong Province
Research Foundation for the Doctoral Program of Liaocheng University