The objective of this study was to evaluate the effects of different cleaning and conditioning procedures after contamination on the tensile bond strength (TBS) of a luting resin to a core build-up composite resin. Specimens (n = 384) made of a core build-up material were stored for 3 weeks in 37 °C water. Half of the specimens were contaminated with saliva and a disclosing silicone and then cleaned either using phosphoric acid, a pumice suspension, air-abrasion with alumina or polishing powder. Surface conditioning was performed by either using a dentin adhesive, a silane containing primer or a composite resin primer, which resulted in 24 unique combinations of 16 specimens per group. Before measuring TBS, half of the specimens of each group were stored in 37 °C water for 3d or were artificially aged for 150 days. Results show that cleaning with pumice or air-abrasion are superior methods compared to using a polishing powder or phosphoric acid. Silane is an inferior conditioning agent compared to composite or dentin primers. Ideally, after contamination, bonding surfaces should be cleaned with a pumice suspension and conditioned with a dentin adhesive. Those surfaces could also be cleaned and conditioned with air-abrasion with alumina particles and a composite resin primer.
Subject
General Materials Science
Reference49 articles.
1. Guidelines for the preparation of CAD/CAM ceramic inlays and partial crowns;Ahlers;Int. J. Comput. Dent.,2009
2. Effect of crown preparation height on the retention and resistance of gold castings;Maxwell;Gen. Dent.,1990
3. Influence of restoration thickness and dental bonding surface on the fracture resistance of full-coverage occlusal veneers made from lithium disilicate ceramic
4. In vivo study of the marginal integrity of composite resin buildups after full crown preparation;Wegner;J. Adhes. Dent.,2004
5. Influence of metal cleaning methods on the resin bond strength to NiCr alloy
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献