Abstract
This paper discusses the features of ω-phase formation and its thermal stability depending on the phase composition, alloying element and the grain size of the initial microstructure of Ti–Nb and Ti–Mo alloys subjected to high-pressure torsion (HPT) deformation. In the case of two-phase Ti–3wt.% Nb and Ti–20wt.% Nb alloys with different volume fractions of α- and β-phases, a complete β→ω phase transformation and partial α→ω transformation were found. The dependence of the α→ω transformation on the concentration of the alloying element was determined: the greater content of Nb in the α-phase, the lower the amount of ω-phase that was formed from it. In the case of single-phase Ti–Mo alloys, it was found that the amount of ω-phase formed from the coarse-grained β-phase of the Ti–18wt.% Mo alloy was less than the amount of the ω-phase formed from the fine α′-martensite of the Ti–2wt.% Mo alloy. This was despite the fact that the ω-phase is easier to form from the β-phase than from the α- or α′-phase. It is possible that the grain size of the microstructure also affected the phase transformation, namely, the fine martensitic plates more easily gain deformation and overcome the critical shear stresses necessary for the phase transformation. It was also found that the thermal stability of the ω-phase in the Ti–Nb and Ti–Mo alloys increased with the increasing concentration of Nb or Mo.
Funder
National Science Center
Russian Ministry of Science and Higher Education
Subject
General Materials Science
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献