Abstract
This work investigated the (0002) textured ZnO films without and with the addition of an Au continuous top layer and its effects on their surface wettability and plasmonic resonance characteristics. The ZnO films were directly fabricated onto glass substrates at the synthesized temperature of 300 °C via a plasma-enhanced chemical vapor deposition (PECVD) system, and the as-synthesized ZnO film exhibited an average optical transmittance value of 85%. The ultraviolet (UV) light irradiation can be applied to enhance the hydrophilicity, changing it from a hydrophobic status to hydrophilic status due to the existing and adjustable characteristics of the photocatalytic activity. On the other hand, the surface wetting/contact angle (CA) value of the ZnO film with a controllable surface wettability switched from 94° (hydrophobicity) to 44° (hydrophilicity), after it was exposed to UV light irradiation for 5 min, and stably reversed back to hydrophobicity (92°) via a post-annealed treatment using rapid thermal annealing (RTA) at 350 °C for 5 min in air. A fast, simple, and reversible method for switching between hydrophilic and hydrophobic status is claimed in this present work. The improved surface plasmonic resonance is owning to the coupled electron and photon oscillations that can be obtained and produced at the interface between the flat Au layer and ZnO (metal/metallic oxide) heterostructured films for future applications of various wide-bandgap compound semiconductors.
Funder
Ministry of Science and Technology
Quantum Materials Shared Facilities of the Institute of Physics at Academia Sinica
Subject
Engineering (miscellaneous),Ceramics and Composites
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献