Microstructure Characteristics and Its Effect on the Fracture in the Triple Junction Region of Friction Stir Welded Mg Alloys Subjected to Tension

Abstract

Because of the tensile strength decreasing of the friction stir welded wrought magnesium (Mg) alloy compared to the base material, the reasons for the failure of weld has been focused on. After the fracture in transverse tension, the crack went through the welded joint from the center of the weld to the transition zone between the thermal-mechanical affected zone and weld zone. In the present study, the microstructure characteristics and its effect on the facture in the triple junction region is investigated. Based on the metallography and the electron back-scattered diffraction (EBSD) technology, it was observed that a twin band extended from the triple junction region to the middle of weld. The profuse twinning in the twin band was considered to play an important role on the crack propagation from the stir zone edge to the crown zone.