Clinical Investigation of the Inhibitory Effects of Tooth-Coating Materials on Initial Active Root Caries: A Pilot Randomized Controlled Trial

Abstract

Background and Objectives: Caredyne ZIF-C is a novel, capsule-mixed zinc-containing prototype glass ionomer cement (GIC). Zinc ions are reported to inhibit root dentin demineralization, dentin collagen degradation, bacterial growth, acid production, and in vitro bacterial biofilm formation. However, the effectiveness of GICs against initial root caries lesions is unclear. Therefore, this study aimed to evaluate the efficacy of GICs, especially the new zinc-containing Caredyne ZIF-C GIC, as tooth-coating materials in patients with initial active root caries. Materials and Methods: A total of 58 lesions in 47 older adults (age > 65 years) were randomly allocated to one of the following three groups: Caredyne ZIF-C, Fuji VII (a conventional GIC), and sodium fluoride (NaF). All the lesions were treated with the assigned materials without removing the infected dentin, and the rates of dental plaque attachment and coating material fall-out were evaluated after 3, 6, and 12 months. The failure rate was defined as the number of teeth that needed restoration due to caries progression. Results: The plaque attachment rates tended to be lower in the material-coated root surfaces than in the healthy exposed root surfaces after 3, 6, and 12 months, although the differences among the three groups were not significant. Moreover, the coating material fall-out rate tended to be lower in the Caredyne ZIF-C group than in the Fuji VII group. There was no significant difference in the failure rate among the three groups at the 12 months mark. Conclusions: Though this pilot study offers a new direction for suppressing the progression of initial active root caries by controlling plaque attachment using GICs including Caredyne ZIF-C, clinical studies with a larger sample size are needed.