Microstructure and Mechanical Properties of As-Aged Mg-Zn-Sn-Mn-Al Alloys

Author:

Hou Caihong,Ye Zhisong,Qi FugangORCID,Lu Liwei,She Jia,Wang Lifei,Ouyang Xiaoping,Zhao Nie,Chen Jing

Abstract

The microstructure and mechanical properties of as-aged Mg-6Zn-4Sn-1Mn-xAl (ZTM641-xAl, x = 0, 0.2, 0.5, 1, 2, 3 and 4 wt.%) alloys are studied in this paper. In terms of microstructure, the results reveal that the addition of Al mainly leads to the formation of the Al8Mn5, Al11Mn4, Al2Mg5Zn2 and Mg32(Al,Zn)49 phases. With increases in the addition of Al, the average grain size first decreases and then increases, while the undissolved phases increase. The average grain size of the ZTM641-0.5Al alloy is the smallest, and the single-aged and double-aged grain size is 14 μm and 12 μm, respectively. As for mechanical properties, with increases in the Al element, the strength decreases, and the elongation first increases and then decreases. The double-aged ZTM641-0.2Al alloy exhibits favorable mechanical properties at room temperature, and the UTS, YS and elongation are 384 MPa, 360 MPa and 9%, respectively. Further, the double-aged ZTM641-0.2Al alloy exhibits the comprehensive mechanical properties at 150 °C, that is, the UTS, YS and elongation are 212 MPa, 196 MPa and 29%, respectively, which is about 45% higher than that of the elongation of ZTM641. The ZTM641-xAl alloys exhibits mixed fracture at room temperature, and, with increases in the addition of Al, the fracture mechanisms of alloys are mixed fracture, ductile fracture and mixed fracture at 200 °C.

Funder

National Natural Science Foundation of China

Hunan Provincial Natural Science Foundation of China

Educational Commission of Hunan Province of China

High Technology Research and Development Program of Hunan Province of China

Publisher

MDPI AG

Subject

General Materials Science

Reference40 articles.

1. Preface to the viewpoint set on: The current state of magnesium alloy science and technology;Agnew;Scr. Mater.,2010

2. Towards the development of heat-treatable high-strength wrought Mg alloys;Hono;Scr. Mater.,2010

3. Effects of phase composition on the mechanical properties and damping capacities of as-extruded Mg–Zn–Y–Zr alloys;Wang;J. Alloy. Compd.,2011

4. Influences of Cr on the microstructural, wear and mechanical performance of high-chromium white cast iron grinding balls;Kaya;J. Mater. Manuf.,2022

5. Drilling of AZ31 Magnesium Alloy under dry and cryogenic conditions;Coban;J. Mater. Manuf.,2022

Cited by 2 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3