Abstract
The dielectric function and the bandgap of BiFe0.5Cr0.5O3 thin films were determined from spectroscopic ellipsometry and compared with that of the parent compounds BiFeO3 and BiCrO3. The bandgap value of BiFe0.5Cr0.5O3 is lower than that of BiFeO3 and BiCrO3, due to an optical transition at ~2.27 eV attributed to a charge transfer excitation between the Cr and Fe ions. This optical transition enables new phonon modes which have been investigated using Raman spectroscopy by employing multi-wavelengths excitation. The appearance of a new Raman mode at ~670 cm−1 with a strong intensity dependence on the excitation line and its higher order scattering activation was found for both BiFe0.5Cr0.5O3 thin films and BiFexCr1−xO3 polycrystalline bulk samples. Furthermore, Raman spectroscopy was also used to investigate temperature induced structural phase transitions in BiFe0.3Cr0.7O3.