This study focuses on the development of porous ceramer and SiOC composites which are suitable for microfiltration applications, using a mixture of polysiloxanes as the preceramic precursor. The properties of the membranes—such as their pore size, hydrophilicity, specific surface area, and mechanical resistance—were tailored in a one-step process, according to the choice of pyrolysis temperatures (600–1000 °C) and the incorporation of micro- (SiC) and nanofillers (TiO2). Lower pyrolysis temperatures (<700 °C) allowed the incorporation of TiO2 in its photocatalytically active anatase phase, enabling the study of its photocatalytic decomposition. The produced materials showed low photocatalytic activity; however, a high adsorption capacity for methylene blue was observed, which could be suitable for dye-removal applications. The membrane performance was evaluated in terms of its maximum flexural strength, water permeation, and separation of an oil-in-water emulsion. The mechanical resistance increased with an increase of the pyrolysis temperature, as the preceramic precursor underwent the ceramization process. Water fluxes varying from 2.5 to 370 L/m2·h (2 bar) were obtained according to the membrane pore sizes and surface characteristics. Oil-rejection ratios of 81–98% were obtained at an initial oil concentration of 1000 mg/L, indicating a potential application of the produced PDC membranes in the treatment of oily wastewater.
Funder
Deutsche Forschungsgemeinschaft
Coordenação de Aperfeicoamento de Pessoal de Nível Superior
Subject
Filtration and Separation,Chemical Engineering (miscellaneous),Process Chemistry and Technology
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献