Abstract
This study presents the successful synthesis of a cesium–nickel–vanadium fluoride (CsNiVF6) pyrochlore nano-sheet catalyst via solid-phase synthesis and its electrochemical performance in green hydrogen production through urea electrolysis in alkaline media. The physicochemical characterizations revealed that the CsNiVF6 exhibits a pyrochlore-type structure consisting of a disordered cubic corner-shared (Ni, V)F6 octahedra structure and nano-sheet morphology with a thickness ranging from 10 to 20 nm. Using the CsNiVF6 catalyst, the electrochemical analysis, conducted through cyclic voltammetry, demonstrates a current mass activity of ~1500 mA mg−1, recorded at 1.8 V vs. RHE, along with low-resistance (3.25 ohm) charge transfer and good long-term stability for 0.33 M urea oxidation in an alkaline solution. Moreover, the volumetric hydrogen production rate at the cathode (bare nickel foam) is increased from 12.25 to 39.15 µmol/min upon the addition of 0.33 M urea to a 1.0 KOH solution and at a bias potential of 2.0 V. The addition of urea to the electrolyte solution enhances hydrogen production at the cathode, especially at lower voltages, surpassing the volumes produced in pure 1.0 M KOH solution. This utilization of a CsNiVF6 pyrochlore nano-sheet catalyst and renewable urea as a feedstock contributes to the development of a green and sustainable hydrogen economy. Overall, this research underscores the potential use of CsNiVF6 as a cost-effective nickel-based pyrochlore electrocatalyst for advancing renewable and sustainable urea electrolysis processes toward green hydrogen production.