The phosphors of formula Ba5Si8O21:Eu2+,Dy3+ were synthesized and studied in order to improve their properties. Their synthesis conditions were evaluated as a function of precursors, crucible composition, flux agents, dopants and temperatures. The samples were characterised by means of a systematic investigation through elemental, kinetic, mineralogical (both qualitative and quantitative), and morphological analysis. This study allows for a careful evaluation of the parameters that influence the formation and properties of Ba5Si8O21:Eu2+,Dy3+ phosphors. As for the synthesis conditions, the use of Na2SiO3, BaCO3 and NH4Cl as precursors was very important to reduce the temperature and time of synthesis. The reducing atmosphere produced with purified coal was cheaper and gave results similar to the more traditional gas mixture (H2/N2). At the end of this study, a phosphor with improved long persistent phosphorescence (LPP) characteristics was obtained with Ba/Si = 0.7, Eu/Si = 2.8 × 10−3 and Dy/Si = 3.6 × 10−3 following a 6 h-synthesis in a quartz crucible.
Subject
General Materials Science
Reference38 articles.
1. Luminescent Materials;Blasse,1994
2. Phosphoreszenz und fluoreszenz, in: Handbuch der Experimentalphysik, 23;Lenard,1928
3. Activators and co-activators in calcium sulfide phosphors
4. Electron Traps and Infrared Stimulation of Phosphors
5. Phosphor Handbook;Yen,1998
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献