Abstract
In this study, the short fatigue crack behavior in a precipitation-strengthened CuNi2Si alloy was investigated using a replica technique under rotating bending loads with periodic overloads, an overload ratio of 1.5, and the stress ratio of both was R = −1. The results show that all the fatigue cracks originated from the surface of the specimen and displayed a trend of slow initiation and then rapid propagation. The introduction of overloads significantly reduced the fatigue crack initiation time and the fatigue life of the sample. The average life of the overloaded samples was only 31% that of the constant load samples. For overload specimens, multiple cracks grew at the same time and merged at different stages, causing the crack length to increase instantaneously after they merged, thereby considerably reducing the fatigue life. Fractographical analysis and observation of the surface-etched sample replica film showed that cracks in samples with and without overload both propagated along the grain boundaries.
Funder
National Natural Science Foundation of China
State Key Laboratory of Traction Power
Subject
General Materials Science,Metals and Alloys
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献