Affiliation:
1. School of Materials Science and Chemical Engineering, Ningbo University, Ningbo 315211, China
2. Key Laboratory of Photoelectric Detection Materials and Devices of Zhejiang Province, Ningbo University, Ningbo 315211, China
Abstract
Transparent ceramics (Gd0.975−xLuxDy0.025)3Al5O12 (x = 0.2, 0.5, 0.975) are fabricated by vacuum sintering with the transmittance of ~60% at 583 nm. The doping of Lu3+ was beneficial to stabilize the garnet phase, and the best doping concentration was 20 at.%. All three (Gd, Lu)3Al5O12:Dy ceramics display typical Dy3+ emission, originating from 4F9/2 → 6HJ (J = 15/2, 13/2, 11/2) transition. Temperature-dependent luminescence spectra from 303.15 K to 603.15 K prove that the (Gd, Lu)3Al5O12:Dy ceramics had good thermal stability and could be an ideal yellow-emitting candidate in light-emitting diodes. The luminous efficiency of the encapsulated white LED lamp was found to be ~87.9 lm/W when the injection current was 600 mA. The transparent (Gd, Lu)3Al5O12:Dy ceramics show great application potential in various optical systems especially in the fields of luminescence and display.
Funder
Natural Science Foundation of China
Department of Education of Zhejiang Province
Natural Science Foundation of Ningbo Municipality
Subject
General Materials Science,Metals and Alloys