Effect on the Property of 2195 Al-Li Alloy Laser-Welded Joints with Different Filler Materials

Author:

Xu Bing12,Jin Guobao2,Zhang Zifeng2,Wang Jianfeng1ORCID,Zhan Xiaohong1

Affiliation:

1. College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 211106, China

2. College of Mechanical Engineering, Chao Hu University, Hefei 238024, China

Abstract

In order to improve the performance of welded joints in Al-Li alloys, butt joints consisting of 2 mm thick 2195-T8 Al-Li alloy plates are fabricated by laser beam welding with different filler wires in this paper. The joints welded by ER2319CT, ER4047, and without filler are investigated in the context of microstructure, the distribution of alloying elements, the burning loss of alloying elements, and tensile strength. From the fusion boundary to the center of the weld seam (WS), the crystal morphologies vary in the sequence of fine equiaxed grains, columnar dendrite, and equiaxed dendrite. The equiaxed grains and columnar dendrite disappear in certain areas of the WS by ER2319CT. The burning loss rates of Li and Cu in the WS by filler wires are higher than those by laser welding without filler. AlLiSi and Al2Cu are identified as the strengthening phases in the WS by ER4047, while Al2Cu, Al2CuLi, and Al6CuLi3 are the strengthening phases in the WS by ER2319CT. Compared with laser welding without filler wire, more strengthening phases improve the mechanical properties of the welded joints by filler wires. Both types of welding wires can improve the performance of welded joints, and ER2319CT is more effective.

Funder

the Natural Science Foundation of Guangdong Province

the Key Laboratory Project of the Chaohu University

Key scientific research project of Chaohu University

Publisher

MDPI AG

Subject

General Materials Science,Metals and Alloys

Cited by 2 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3