Affiliation:
1. CISRI HIPEX Technology Co., Ltd., Beijing 100081, China
2. Beijing Advanced Innovation Center for Materials Genome Engineering, Central Iron & Steel Research Institute, Beijing 100081, China
Abstract
Ti-6Al-4V titanium alloy products formed by selective laser melting (SLM) are characterized by high strength and low plasticity. In addition, there may be pores inside the material, which may become a fracture sprouting point and accelerate the failure of the parts. Using an optical microscope (OM), scanning electron microscope (SEM), and electronic universal testing machine, the effects of hot isostatic pressing (HIP) parameters on the microstructure and tensile property of SLM-formed Ti-6Al-4V titanium alloy were investigated. The results show that HIP performed below the β-phase transition temperature, and the structure of the Ti-6Al-4V titanium alloy is composed of an α phase and β phase. With the increase in the HIP temperature, the α lath coarsens into a short rod, the content of the β phase increases and coarsens, and the tensile strength and yield strength of Ti-6Al-4V show a decreasing trend. With an HIP process performed at a temperature of 910 °C and pressure of 130 MPa for 2 h, the Ti-6Al-4V titanium alloy obtains the best matching of strength and plasticity.
Subject
General Materials Science,Metals and Alloys
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献